Nguyen Manh Hung, Dao Viet Thang, Nguyen Thi Dieu Thu, Ho Quynh Anh, Nguyen Cao Khang, Le Thi Mai Oanh, Pham Do Chung, Nguyen Thi Nhung, Lam Thi Hang, Lê Thị Mai Oanh(1), Nguyễn Thị Diệu Thu(2)

ENHANCE A PHOTOCATALYTIC ACTIVITY ON Ag3PO4 BY Ag\Ag3PO4 COMPOSITES

ENHANCE A PHOTOCATALYTIC ACTIVITY ON Ag3PO4 BY Ag\Ag3PO4 COMPOSITES

Tạp chí Khoa học - Trường Đại học Sư phạm Hà Nội: Khoa học Tự nhiên

2023

67

86

In this study, we investigated the formation and influence of Ag particles on the physical properties and photocatalytic performance of Ag3PO4 photocatalysts when Ag particles adhered to the Ag3PO4 surface. The material is prepared by a simple precipitation method with illumination. The properties of the materials were investigated by X-ray diffraction (XRD), Raman scattering, scanning electron microscopy (SEM), UV-vis absorption, and the photocatalytic ability to decompose organic solutions. The results show the vibrational change of the [PO4] group in the structure presented in the Raman scattering spectrum highest RhB decomposition. The experimental results indicated that the Ag\Ag3PO4 showed highly efficient and stable photocatalytic activity under visible light irradiation. The Ag\Ag3PO4 sample with the Ag+\PO43- the ratio of 3.6\1 gave efficiency when stimulated with visible light of Xenon lamps. This sample degraded almost completely to RhB in 10 ppm solution after 15 min of illumination, with a decomposition rate of 0.241 min-1.

In this study, we investigated the formation and influence of Ag particles on the physical properties and photocatalytic performance of Ag3PO4 photocatalysts when Ag particles adhered to the Ag3PO4 surface. The material is prepared by a simple precipitation method with illumination. The properties of the materials were investigated by X-ray diffraction (XRD), Raman scattering, scanning electron microscopy (SEM), UV-vis absorption, and the photocatalytic ability to decompose organic solutions. The results show the vibrational change of the [PO4] group in the structure presented in the Raman scattering spectrum highest RhB decomposition. The experimental results indicated that the Ag\Ag3PO4 showed highly efficient and stable photocatalytic activity under visible light irradiation. The Ag\Ag3PO4 sample with the Ag+\PO43- the ratio of 3.6\1 gave efficiency when stimulated with visible light of Xenon lamps. This sample degraded almost completely to RhB in 10 ppm solution after 15 min of illumination, with a decomposition rate of 0.241 min-1.