NGHIÊN CỨU CẤU TRÚC, TÍNH CHẤT ĐẶC TRƯNG CỦA VẬT LIỆU NANOCOMPOSITE CARBON AEROGEL/TiO2/CNTs ỨNG DỤNG LÀM ĐIỆN CỰC CHO THIẾT BỊ KHỬ MẶN THEO CÔNG NGHỆ ĐIỆN DUNG (CDI)

STUDYING THE STRUCTURE AND CHARACTERISTIC PROPERTIES OF CARBON AEROGEL/TiO2/CNTs NANOCOMPOSITE MATERIALS APPLIED AS ELECTRODE FOR CAPACITIVE DESOLVATION EQUIPMENT (CDI)

Tạp chí Phân tích Hóa, Lý và Sinh học

2024

2A

261

In this study, carbon aerogel (CA) from sugarcane bagasse, TiO2 and carbon nanotube were fabricated to nanocomposite to be used as electrode for desalination equipment using CDI capacitive technology. CA/TiO2/CNTs nanocomposite material has advantages due to inheriting properties from CA materials such as high surface area, electrochemical stability of TiO2 and high electrical conductivity of CNTs. The CA/TiO2-30/CNTs-5 nanocomposite has outstanding capacitance reaching 167 F/g and high charge-discharge durability of 1000 cycles. Investigating the desalination ability, the CA/TiO2-30/CNTs-5 electrode achieved a high salt adsorption capacity value of ~21 mg/g with a fast salt adsorption rate at a potential of 1.4 V.

In this study, carbon aerogel (CA) from sugarcane bagasse, TiO2 and carbon nanotube were fabricated to nanocomposite to be used as electrode for desalination equipment using CDI capacitive technology. CA/TiO2/CNTs nanocomposite material has advantages due to inheriting properties from CA materials such as high surface area, electrochemical stability of TiO2 and high electrical conductivity of CNTs. The CA/TiO2-30/CNTs-5 nanocomposite has outstanding capacitance reaching 167 F/g and high charge-discharge durability of 1000 cycles. Investigating the desalination ability, the CA/TiO2-30/CNTs-5 electrode achieved a high salt adsorption capacity value of ~21 mg/g with a fast salt adsorption rate at a potential of 1.4 V.