Khảo sát ảnh hưởng của một số chất xúc tác amin họ Amidazol đến quá trình đóng rắn của dầu lanh Epoxy hóa bằng Anhydrit 4-Metylhexahydrophtalic. Phần 2: Khảo sát ảnh hưởng của 2-etyl-4-metylimidazol và 1,2-Dimetylimidazol đến quá trình đóng rắn dầu lanh e

Study on the effect of imidazole catalysts on curing process of the epoxy linseed oil by 4-methylhexahydrophthalic anhydride. Part 2- Study on the effect of 2-ethyl-4-methylimidazole and 1,2-dimethylimidazole on curing process of epoxidized linseed oil by

Hóa học

2014

6

713-716

0866-7144

Dầu lanh epoxy hóa đóng rắn, 2-etyl-4-metylimidazol, 1,2-dimetylimidazol, Nhựa bioepoxy, Anhydrit 4-Metylhexahydrophtalic

In this study, the effect of the imidazole amine catalysts such as 2-ethyl-4-metylimidazol (EMI) and 1,2-Dimethylimidazol (DMI) on the curing process and curing kinetics of the epoxidized linseed oil (ELO) by 4methylhaxahydrophtalic anhydride (MHHPA) has been investigated. The change of temperature vs. curing time was carried out in thermal measuring instrument. Gel content was determined by method of acetone extraction on Soxhlet instruments and Origin software version 9.0 was used to survey the curing process. The results show that, two kinds of above catalyst can be used to promote for the curing process of ELO. In which, using EMI catalyst shows moderate reaction between epoxy group of ELO and anhydride. Inverserly, in the presence of DMI catalyst, the curing process of ELO occurs fastly with high maximum temperature of exothermic. The rising of gel content and curing rate of bioepoxyresin in the presence of DMI catalyst were higher than compare with EMI catalyst.